Abstract
Herein, bimetal nickel-cobalt phosphate (NiCoP) nanostructures coated on nickel foam (NF) were synthesized for hybrid supercapacitors by a facile one-step potentiostatic electrodeposition method. The optimization of the capacitive performance for supercapacitors was achieved by varying the deposition time from 5 to 20 min. When the electrodeposition time was 15 min, an optimal performance with the NiCoP/NF-2 was achieved. A specific capacity of 883 C·g−1 was recorded at a current density of 1 A·g−1, a best rate performance of 87% along with a highest coulombic efficiency of 100%, revealing good capacitive performance and excellent reversibility. Furthermore, NiCoP/NF-2 was assessed as a positive electrode in a hybrid supercapacitor. Using activated carbon (AC) as a negative electrode, the assembled device exhibited an energy density of 54 Wh·kg−1 at a power density of 2.7 kW·kg−1 with a large working potential window of 0–1.8 V. After charging to 3.6 V for 19 s, two hybrid supercapacitor devices connected in series could light up a red LED for 191 s, which indicates that the proposed electrodeposition synthesis process and the prepared NiCoP composites hold high potential for applications in the field of energy storage technology.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.