Abstract
Al-Si dealloying method is widely used to prepare Si anode for alleviating the issues caused by a drastic volume change of Si-based anode. However, this method suffers from the problems of low Si powder yield (<20wt.% Si) and complicated cooling equipment due to the hindrance of large-size primary Si particles. Here, a new modification strategy to convert primary Si to 2D SiOx nanosheets by introducing a Ca modifier into Al-Si alloy melt is presented. The thermodynamics calculation shows that the primary Si is preferentially converted to CaAl2Si2 intermetallic compound in Al-Si-Ca alloy system. After the dealloying process, the CaAl2Si2 is further converted to 2D SiOx nanosheets, and eutectic Si is converted to 3D Si, thus obtaining the 2D SiOx-3D Si hybrid Si-based materials (HSiBM). Benefiting from the modification effect, the HSiBM anode shows a significantly improved electrochemical performance, which delivers a capacity retention of over 90% after 100 cycles and keeps 98.94% capacity after the rate test. This work exhibits an innovative approach to produce stable Si-based anode through Al-Si dealloying method with a high Si yield and without complicated rapid cooling techniques, which has a certain significance for the scalable production of Si-based anodes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.