Abstract
Ti3+ self-doped TiO2 nanosheets with dominant {001} facets for excellent visible-light photocatalytic activity were prepared by a facile one-pot hydrothermal reaction strategy using tetrabutyl titanate (TBT) as titanium source, hydrofluoric acid (HF) as structure-directing agent and zinc powder (Zn) as reductant. The synthesized catalysts were characterized by transmission electron microscope (TEM), X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectra (XPS), diffuse reflectance spectrum (DRS) and nitrogen adsorption–desorption isotherms. The photocatalytic activity of the photocatalyst was evaluated by measure the formation rate of photo-induced hydroxyl radicals (OH) under visible-light irradiation (λ=420±10nm) using coumarin as a probe. It was found that the presence of zinc shows little effect on the morphology, phase structure, BET surface areas and pore structure. However, the addition of Zn powder resulted in the formation of Ti3+ self-doped anatase TiO2 nanosheets with dominant {001} facets, which is responsible for the enhanced visible-light photocatalytic activity. The sample prepared with zinc/TBT molar ratio of 0.3 showed the highest visible-light photocatalytic activity, which is 1.9 times higher than that of commercial P25 TiO2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.