Abstract
Herein, sandwich structured tungsten trioxide (WO3) nanoplate arrays were first synthesized for photoelectrochemical (PEC) water splitting via a facile hydrothermal method followed by an annealing treatment. It was demonstrated that the annealing temperature played an important role in determining the morphology and crystal phase of the WO3 film. Only when the hydrothermally prepared precursor was annealed at 500 °C could the sandwich structured WO3 nanoplates be achieved, probably due to the crystalline phase transition and increased thermal stress during the annealing process. The sandwich structured WO3 photoanode exhibited a photocurrent density of 1.88 mA cm(-2) and an incident photon-to-current conversion efficiency (IPCE) as high as 65% at 400 nm in neutral Na2SO4 solution under AM 1.5G illumination. To our knowledge, this value is one of the best PEC performances for WO3 photoanodes. Meanwhile, simultaneous hydrogen and oxygen evolution was demonstrated for the PEC water splitting. It was concluded that the high PEC performance should be attributed to the large electrochemically active surface area and active monoclinic phase. The present study can provide guidance to develop highly efficient nanostructured photoelectrodes with the favorable morphology.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.