Facile fabrication of 3D-α-Fe2O3@2D-g-C3N4 heterojunction composite materials: Effect of iron oxide loading on the electrochemical performance

Abstract

Designing heterojunction nanocomposites is crucial for optimizing supercapacitor electrodes. This study addresses the challenge by introducing a facile synthesis method for creating 3D-α-Fe2O3@2D-g-C3N4 heterojunctions through a bulk carbon nitride-assisted hydrothermal process. During this process, the growth of ferric oxide particles coincides with the exfoliation and deposition of carbon nitride, leading to simultaneous structural changes in both iron oxide and carbon nitride phases. The resulting composite's properties strongly correlate with the iron oxide loading. Comprehensive characterization using XRD, FTIR, SEM-EDAX, XPS and TEM identified three distinct structures for α-Fe2O3/g-C3N4 composites based on iron oxide loading: low, medium, and high. The medium-loaded sample demonstrated superior electrochemical performance, attributed to better interfacial contact and the formation of 3D-Fe2O3@2D-g-C3N4 heterojunctions. This composite, with an optimized 22 wt% iron oxide loading, exhibited a maximum specific capacitance of 925.1 Fg−1 at 5 mVs−1 and 498.6 Fg−1 at 6 Ag−1 in charge-discharge analysis, with stable performance over 2000 cycles. Overall, this research presents an enhanced hydrothermal method for facile preparation of effective α-Fe2O3/g-C3N4 heterojunction materials.