We showed well-aligned zinc oxide (ZnO) nanorod arrays synthesized using hydrothermal method at atmospheric pressure. The influence of fabrication conditions such as Zn2+/hexamethylentriamin concentration ratio, and growth temperature on the formation of ZnO nanorods was investigated. Scanning Electron Microscope (SEM) images and X-ray Diffraction (XRD) analysis were used to confirm the single crystal of ZnO nanorods, which showed wurtzite structure with growth direction of [0001] (the c-axis). Photoluminescence (PL) measurements of ZnO nanorods revealed an intense ultraviolet peak at 388.5 nm (3.19 eV) at room temperature. The results showed that the ZnO seed layers had strong influence on the growth of vertically aligned ZnO nanorods. The gas sensor based on ZnO nanorod arrays had the most selectivity with n-butanol gas (within 2 surveyed gas: ethanol and n-butanol) and showed a higher sensitivity of 222, fast response time of 15 seconds, recovery time of 110 seconds and lower operating temperature of 200-250 °C than the sensor based on the ZnO film in the same detecting conditions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.