Abstract
The 3-layers accumulative roll bonding process (ARB) has been attempted to increase the strength of copper alloy (Cu-0.02wt.%P) by refining grain size. The 3-layers accumulative roll bonding was conducted up to 7 cycles at room temperature without lubrication. Microstructural evolution of the copper alloy with the number of the 3-layers ARB cycles was investigated by optical microscopy (OM), transmission electron microscopy (TEM), and electron back scatter diffraction (EBSD). The average grain size has been refined from 20 μm before ARB to 170 nm after 7 cycles of 3-layers ARB. More than 70% of ultrafine grains formed by 3-layers ARB were composed of high angle grain boundaries. The average misorientation angle of ultrafine grains was 30.7 degrees in the center of the specimen. Tensile strength after 7 cycles of 3-layers ARB was 605 MPa, which is about 3.2 times higher than the initial value.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.