Fabrication of transparent polymer-matrix nanocomposites with enhanced mechanical properties from chemically modified ZrO2 nanoparticles

Abstract

Optically transparent nanocomposites with enhanced mechanical properties were fabricated using stable dispersions of sub 10 nm ZrO2 nanoparticles. The ZrO2 dispersions were mixed with a commercially available bisphenol-A-based epoxy resin (RIMR 135i) and cured with a mixture of two amine-based curing agents (RIMH 134 and RIMH 137) after complete solvent removal. The colloidal dispersions of ZrO2 nanoparticles, synthesized through a non-aqueous approach, were obtained through a chemical modification of the ZrO2 nanoparticle surface, employing different organic ligands through simple mixing at room temperature. Successful binding of the ligands to the surface was studied utilizing ATR–FT-IR and thermogravimetric analysis. The homogeneous distribution of the nanoparticles within the matrix was proven by SAXS and the observed high optical transmittance for ZrO2 contents of up to 8 wt%. Nanocomposites with a ZrO2 content of only 2 wt% showed a significant enhancement of the mechanical properties, e.g., an increase of the tensile strength and Young’s modulus by up to 11.9 and 12.5%, respectively. Also the effect of different surface bound ligands on the mechanical properties is discussed.