Abstract
Highly transparent MgAl2O4 ceramics have been fabricated by aqueous gelcasting combined with cold isostatic pressing (CIP), pressureless sintering and hot isostatic pressing (HIP) from high purity spinel nanopowders. The gelling system used AM and MABM as monomer and gelling agent. The influences of dispersant and PH on the rheological behavior of the MgAl2O4 slurries were investigated. The spinel slurry with low solids loading (25 vol%) and low viscosity (0.15 Pa s) was obtained by using 6 wt% Duramax-3005 (D-3005) as dispersant. After CIP, the green body had a relative density of 48% with a narrow pore size distribution. The influence of sintering temperature on densification and microstructure was studied, choosing 1500 °C as the sintering temperature. After HIP (1650 °C/177 MPa/5 h), transparent MgAl2O4 ceramic with the thickness of 3 mm was obtained, whose in-line transmittance was 86.4% at 1064 nm and 79.8% at 400 nm, respectively. The ceramic exhibited a dense microstructure with the average grain size of 23 μm. The Vickers hardness and flexure strength of the sample reached 13.6 GPa and 214 MPa, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.