Abstract
To improve fracture strength and fracture toughness in ceramic materials, we focused our attention on an intra-type structure of nanocomposites. We proposed new processing method for fabricating intra-type nanocomposites. In this work, Al2O3/Ni nanocomposites were fabricated using a soaking method and sintered by PECS(Pulse Electric Current Sintering) method. We also estimated seed effects on this system. Seeded nanocomposites showed high fracture strength and higher fracture toughness than non-seeded nanocomposites and monolithic alumina. The fracture strength of the seeded nanocomposites was more than 800MPa in all sintering temperature range. The maximum value of the fracture toughness was 5.5 MPa⋅m1/2 for the specimen sintered at 1350°C. The sintered specimens with high fracture strength and high fracture toughness were annealed from 800°C to 1000°C for 0 to 10 min. The specimen annealed at 800°C for 5 min showed the highest fracture toughness of 7.6 MPa⋅m1/2. This value is two times higher than that of the monolithic alumina.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.