Abstract
CuInGaSe (CIGS) mixed-source was prepared by hydride vapor transport method (HVT). The new source synthesis method was attempted by mixing several metals such as Cu, In, Ga, and Se with 3:5:1:4 mass ratios. This mixed-source was soaked at 1090 °C for 90 min in nitrogen atmosphere. Then, the CIGS was grinded up and formed the state of powder and the CIGS pellet was made by pressure machine. The diameter of pellet is 10 mm. The CIGS thin film was deposited on soda lime glass with evaporated molybdenum layer by e-beam evaporating this CIGS pellet. For crystallization of CIGS thin film, we measured scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), and X-ray diffraction (XRD). High intensity X-ray peaks diffracted from (112), (204)/(220), (116)/(312), and (400) of CIGS thin film and from (110) of Mo were confirmed by XRD measurement.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.