Abstract
Transparent MgO ceramics were fabricated by spark plasma sintering (SPS) of the commercial MgO powder using LiF as the sintering additive. Effects of the additive amount and the SPS conditions (i.e., sintering temperature and heating rate) on the optical transparency and microstructure of the obtained MgO ceramics were investigated. The results showed that LiF facilitated rapid densification and grain growth. Thus, the MgO ceramics could be easily densified at a moderate temperature and under a low pressure. In addition, the transparency and microstructure of the MgO ceramics were found to be strongly dependent on the temperature and heating rate. For the MgO ceramics sintered at 900°C for 5min with the heating rate of 100°C/min and the pressure of 30MPa from the powders with 1wt% LiF, the average in-line transmittance reached 85% in the range of 3–5μm, and the average grain size is ∼0.7μm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.