Fabrication of semi-aromatic polyamide/spherical mesoporous silica nanocomposite reverse osmosis membrane with superior permeability

Abstract

Semi-aromatic polyamide (SAP)/spherical mesoporous silica nanocomposite reverse osmosis (RO) membrane was successfully fabricated using m-phenylene diamine aqueous solution and cyclohexane-1,3,5-tricarbonyl chloride/mesoporous-silica-sphere (MSS) organic solution as main raw materials. The experimental suggests that the microstructures and surface features are significantly different from those of the contrast samples (the full- and semi-aromatic polyamide membranes), including the surface morphology, polymer framework structure, surface charge density, hydrophilicity, and the thickness of barrier layer. It was observed that many MSSs with ca. 1.5nm of pore size are evenly embedded on the surface of the fabricated SAP/MSS RO membrane. Furthermore, the separation performance testing results indicate that the permeabilities range from 62.53 to 72.73L/m2h with the increase of the introduced MSSs from 0.02 to 0.08w/v % under 1.5MPa operating pressure and 2000mg/L NaCl solution, which is obviously better than the contrast samples. Simultaneously, their salt rejections can be still maintained at a comparable level (94.78–91.46%). The excellent separation performance of the nanocomposite RO membrane is closely related to the higher-freedom-degree semi-aromatic framework, the incorporation of MSSs, the improved surface hydrophilicity, the thinner barrier layer, and the enhanced surface negative charge density.