Abstract
Recently, development of porous calcium phosphates ceramics has raised considerable interest. A porous structure promotes cell attachment, proliferation and provides pathways for biofluids. Therefore, a high porosity with interconnected pore structure generally favors tissue regeneration. In this work, replication of 0, 2, 5, 10 and 15% SrHA (strontium-doped hydroxyapatite) porous scaffolds via polymeric sponge method has been employed using the sol-gel derived SrHA powders. To prepare the porous samples, the synthesized SrHA powders were mixed with distilled water and dispersing agent followed by drying in the ambient air and specific sintering process. Morphological evaluation by FESEM measurement revealed that the SrHA scaffolds were characterized by macro-micro interconnected porosity, which replicates the morphology of the cancellous bone. Compression test on the porous scaffolds revealed that doping 10 mol% of strontium in HA has increased the compressive strength by a factor of two compared to the undoped HA with 1.81±0.26 MPa at 41% porosity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.