Abstract
A biodegradable PLA (poly-lactic acid) microneedle having high aspect ratio of over 10, e.g., 100 μm in diameter and 1,000 μm (1 mm) in length, was successfully fabricated using thermal nanoimprint method first in the world. First, optimal conditions for fabricating a conical shape, which is assuming a microneedle tip, were preliminarily investigated. Both in vacuum and under atmospheric pressure, pressure of 20 MPa and temperature of 160 °C were necessary. Next, fabrication of a long microneedle was investigated. As compared to the conical shape, higher pressure of 25 MPa and higher temperature of 166 °C were required. By adjusting the releasing temperature around 98 °C, fabrication of a long microneedle having a smooth surface and no deformation, e.g., no bending, was successfully achieved. It was confirmed that the needle surely can puncture the skin and blood vessel of a mouse.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call