Abstract
A lotus-type porous carbon steel with cylindrical pores was fabricated by the continuous zone melting method in a pressurized mixture of hydrogen and helium gases. The porosity increases with increasing partial pressure of the hydrogen gas, while the pore diameter remains almost constant, independent of the pressure. The ultimate tensile strength of the specimen with cylindrical pores parallel to the tensile direction is lower than the estimated value, assuming that the strength is decreased in proportion to the decrease of the cross-sectional area of the specimen, while the yield strength is higher than the estimated value. The compressive yield strength is also higher than the estimated value. The increase in yield strength is considered to be due to precipitation strengthening. The tensile strength is increased by quenching and tempering, while the elongation decreases. Such mechanical properties are discussed in terms of the microstructural analysis.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.