Abstract
Well-cubic perovskite lanthanum aluminate (LaAlO(3)) film on (110) silicon substrate was fabricated by sol-gel method with corresponding inorganic salts. Lanthanum acetate and aluminum acetate glacial acetic acid solutions were prepared via ligand exchange starting from lanthanum nitrate hexahydrate and aluminum nitrate hexahydrate after being refluxed. (CH(3)CO)(2)O removed nitrates and the crystallized H(2)O completely, acetylacetone (AcAc) was partially bidentated with metallic ion of the metallic acetates and formed La(OAc)(3-x)(AcAc)(x), which were hydrolyzed into La(AcAc)(3-x)(OH)(x) by adding 10 ml 0.4% methyl cellulose (MCL) solution. The La(AcAc)(3-x)(OH)(x), polymerizing and combining with MCL, formed the LaAlO(3) sol precursor with heteropolymeric structure and formed film easily. The epitaxial LaAlO(3) film on Si(110) substrate was crystallized after being annealed in thermal annealing furnace for 650-750 degrees C/30 min. The mor-phologies and microstructures were characterized. The refractive index of the LAO film was 1.942 to 2.007; the dielectric constant and the dissipation factors were estimated to be 23-26 and 2.1x10(-4) - 2.4x10(-4) respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.