Abstract
β-Tricalcium phosphate [β-TCP] is the typical bone substitute due to its excellent osteoconductivity and bioresorbability. One of the keys to improve its potential as bone substitute is to introduce porous structure and its regulation. In this study, interconnected porous β-TCP blocks were fabricated through a setting reaction of β-TCP granules and subsequent heat treatment. First, β-TCP granules were mixed with HNO3 . Upon mixing, β-TCP granules were bridged with dicalcium phosphate dihydrate [DCPD: CaHPO4 ·2H2 O] containing Ca(NO3 )2 . Then, the DCPD-bridged β-TCP was heated at 1100°C. During the heating process, DCPD containing Ca(NO3 )2 transformed into β-TCP and bonded with β-TCP granules. As a result, an interconnected porous β-TCP block formed. The diametral tensile strength and porosity of the interconnected porous β-TCP block fabricated from 200-300-μm β-TCP granules and 5 N HNO3 and then heated at 1,100°C were 1.4 ± 0.2 MPa and 57% ± 2%, respectively. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 106A: 797-804, 2018.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.