Abstract
Ti2AlN/TiAl composites with different volume fractions of reinforcement were successfully fabricated by hot-pressing sintering method (reaction hot pressing) using Ti, Al and TiN powders as starting materials. The synthesis process includes four stages: first, the reactions between Al and Ti powers and between Al and TiN powders respectively occur and result in TiAl3 phase; secondly, Al powders in the sample are exhausted; the remaining Ti cores react with TiAl3 layer to form Ti-Al intermetallics; moreover, a few Ti2AlN particles precipitate from the TiAl3 phase; thirdly, Ti-Al intermetallics react with the remaining Ti cores to form Ti3Al and TiAl phases. TiAl phase and original TiN powers are in direct contact each other; finally, the residual TiN powers react with TiAl phase and result in a plenty of Ti2AlN phase. Compared with TiAl matrix, the hardness, elastic modulus and high-temperature compressive strength of Ti2AlN/TiAl composite are improved obviously and they are all enhanced with increasing the volume fraction of Ti2AlN phase.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.