Abstract
Anti-reflection coating films have used to increase the transmittance of displays and enhance the efficiency of solar cells. Hydrophobic anti-reflection coating films were fabricated on a glass substrate by sol-gel method. To fabricate an anti-reflection film with a high transmittance, poly ethylene glycol (PEG) was added to tetraethyl orthosilicate (TEOS) solution. The content of PEG was changed from 1 to 4 wt% in order to control the morphology, thickness, and refractive index of the SiO2 thin films. The reflectance and transmittance of both sides of the coated thin film fabricated with PEG 4 wt% solution were 0.3% and 99.4% at 500 nm wavelength. The refractive index and thickness of the thin film were n = 1.29 and d = 105 nm. Fluoro alkyl silane (FAS) was used for hydrophobic treatment on the surface of the anti-reflection thin film. The contact angle was increased from 13.2˚ to 113.7˚ after hydrophobic treatment.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.