Abstract
A simple approach to fabricate hollow silica nanorods is reported, using nanocrystalline cellulose (NCC) as templates. Uniform NCC with the length of ca. 100 nm and a diameter of ca. 10 nm were prepared by hydrolysis of microcrystalline cellulose (MCC) in strong sulfuric acid condition. NCC was used as a template to prepare a core-shell composite of silica and NCC. The sol-gel reaction of tetraethyl orthosilicate (TEOS) was employed to coat NCC with a nano thickness of silica in the presence of ammonia. Finally, hollow silica nanorods were obtained by calcination of the composite at 600°C to remove the organic cellulose template completely. The obtained hollow silica nanorods were found to have uniform size and shape: with a length of ca. 100 nm, an inner diameter close to the original diameter of NCC, and a thickness of around 10 to 15 nm. These results suggest that NCC is an excellent template for manufacturing nano hollow materials with uniform shape and size.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.