Fabrication of highly ordered anodic aluminium oxide templates on silicon substrates

Abstract

The controlled fabrication of highly ordered anodic aluminium oxide (AAO) templates of unprecedented pore uniformity directly on Si, enabled by new advances on two fronts – direct and timed anodisation of a high-purity Al film of unprecedented thickness (50 µm) on Si, and anodising a thin but pre-textured Al film on Si, has been reported. To deposit high-quality and ultra-thick Al on a non-compliant substrate, a prerequisite for obtaining highly ordered pore arrays on Si by self-organisation while retaining a good adhesion, a specially designed process of e-beam evaporation followed by in situ annealing has been deployed. To obtain an AAO template with the same high degree of ordering and uniformity but from a thin Al film, which is not achievable by the self-organisation alone, pre-patterning of the thin Al surface by reactive ion etching using a free-standing AAO mask that was formed in a separate process was performed. The resultant AAO/Si template provides a good platform for integrated growth of nanotube, nanowire or nanodot arrays on Si. Template-assisted growth of carbon nanotubes (CNTs) directly on Si was demonstrated via a chemical vapour deposition method. By controllably removing the AAO barrier layer at the bottom of the pores and partially etching back the AAO top surface, new CNT/Si structures were obtained with potential applications in field emitters, sensors, oscillators and photodetectors.