Abstract
The high production flexibility of laser additive manufacturing is a significant advantage in the fabrication of functionally graded materials such as TC4 alloy and 30CrNi2MoVA steel, which have applications in the nuclear and aerospace industries. A laser melting deposition (LMD) process was employed to bond TC4 alloy with a high-strength 30CrNi2MoVA steel by the insertion of different intermediate materials, the intermediate materials consisted of either a pure-V layer or a V/Cu composite layer. The microstructure, elements distribution, phase composition, and mechanical properties of the joints were characterized. The appropriate transition interlayer composition was determined using ThermoCalc software. The experimental results indicated that using a pure V interlayer to bond TC4 with steel via LMD was extremely difficult, due to the generation of Fe-Ti intermetallic compounds. Consequently, the maximum tensile strength was only 58 ± 14 MPa. However, the V/Cu composition transition interlayer successfully suppressed the diffusion and mixing of Ti and Fe during LMD, forming joints between TC4 alloy and 30CrNi2MoVA steel with a tensile strength of 191 ± 20 MPa. In summary, this paper reports a new route to prepare a relatively strong TC4/30CrNi2MoVA dissimilar joint by the insertion of a V/Cu composite transition interlayer that does not require additional supplementary processes and does not limit the component geometry.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.