Abstract
We report the fabrication of high aspect ratio, sub-10 nm size, structures in silicon without involving any wet chemical etching. A 50 nm thick double layer of low and high molecular weight polymethylmethacrylate resist was exposed with an 80 kV electron beam of diameter smaller than 5 nm. After exposure the resist was developed in 3:7 cellusolve: methanol with ultrasonic agitation during development. A 5 nm thick AuPd film was deposited by ionized beam evaporation and a metal pattern was obtained by liftoff. Sub-10 nm AuPd dots were recorded with a scanning electron microscope. The AuPd pattern was then used as a mask on the Si substrate which was etched with reactive ion etching. Silicon nanocolumns with diameters ranging from 5 to 7 nm and an aspect ratio of height to diameter of about 7:1 were obtained.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.