Laser grade 7 at.% Er:Y2O3 transparent ceramics with submicron grain size were fabricated by using one-step vacuum sintering followed by hot isostatic pressing (HIPing) technique. Through studying the sintering trajectory of Er:Y2O3 ceramics, the sintering temperature zone where sufficient relative density (>96%), no pore-boundary separation, and sub-micron grain size (<1 μm) ceramic samples could be identified. The samples pre-sintered in this zone were readily densified by HIPing. To maximum the densification and achieve high transparency, it is critical to suppress the final-stage grain growth. After HIPing at 1520 °C, the Er:Y2O3 ceramics were fully densified without further grain growth, and exhibited in-line transmission of about 81.6% at 2000 nm. Continuous wave (CW) room temperature laser operation of the Er:Y2O3 transparent ceramic at 2.7 μm was demonstrated.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.