Fabrication of different pore shapes by multi-step etching technique in ion-irradiated PET membranes

Abstract

A method for the fabrication of different pore shapes in polyethylene terephthalate (PET)-based track etched membranes (TEMs) is reported. A multi-step etching technique involving etchant variation and track annealing was applied to fabricate different pore shapes in PET membranes. PET foils of 12-μm thickness were irradiated with Bi ions (kinetic energy 9.5MeV/u, fluence 106ions/cm2) at the Heavy Ion Research Facility (HIRFL, Lanzhou). The cross-sections of fundamental pore shapes (cylinder, cone, and double cone) were analyzed. Funnel-shaped and pencil-shaped pores were obtained using a two-step etching process. Track annealing was carried out in air at 180°C for 120min. After track annealing, the selectivity of the etching process decreased, which resulted in isotropic etching in subsequent etching steps. Rounded cylinder and rounded cone shapes were obtained by introducing a track-annealing step in the etching process. Cup and spherical funnel-shaped pores were fabricated using a three- and four-step etching process, respectively. The described multi-step etching technique provides a controllable method to fabricate new pore shapes in TEMs. Introduction of a variety of pore shapes may improve the separation properties of TEMs and enrich the series of TEM products.