Abstract
Endothelialization of biomaterials is a promising way to prevent intimal hyperplasia of small-diameter vascular grafts. The aim of this study was to design a nanofiber mesh (NFM) that facilitates viability, attachment and phenotypic maintenance of human coronary artery endothelial cells (HCAECs). Collagen-coated poly( l-lactic acid)- co-poly( ε-caprolactone) P(LLA-CL 70:30) NFM with a porosity of 64–67% and a fiber diameter of 470±130 nm was fabricated using electrospinning followed by plasma treatment and collagen coating. The structure of the NFM was observed by SEM and TEM, and mechanical property was studied by tensile test. The presence of collagen on the P(LLA-CL) NFM surface was verified by X-ray photoelectron spectroscopy (XPS) and quantified by colorimetric method. Spatial distribution of the collagen in the NFM was visualized by labelling with fluorescent probe. The collagen-coated P(LLA-CL) NFM enhanced the spreading, viability and attachment of HCAECs, and moreover, preserve HCAEC's phenotype. The P(LLA-CL) NFM is a potential material for tissue engineered vascular graft.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.