Fabrication of Bi–Sb–Te Thermoelectric by Cold-Pressed Sintering for Motorcycle Exhaust.

Abstract

This study was conducted on the Bi–Sb–Te thermoelectric material which is cold-pressed Sintering under 750 Mpa to make square thermoelectric pairs with size 8.2 mm × 8.2 mm and thicknesses 0.8 mm and 1.5 mm. The zone melting method was used to acquire P-type thermoelectric material Bi0.4Sb1.6Te3 and N-type thermoelectric material Bi2Te2.5Se0.5. At temperature 383 K, the measured Seebeck coefficient of Bi0.4Sb1.6Te3 is 222 μV/K, and its thermoelectric figure of merit ZT is 1.35. At temperature 400 K, the measured Seebeck coefficient of Bi2Te2.5Se0.5 is 210 μV/K, and its thermoelectric figure of merit ZT is 1.13. Using Solder paste Sn42Bi58 and copper electrode plate are in series connection with 16 pieces of P/N thermoelectric material to form thermoelectric modules. The thermoelectric module is actually pasted on the motorcycle waste heat source to be evaluated the performance, making the cold-end temperature dissipation heat can enhance the temperature difference between it so as to increase the output power. Increasing the leg thickness of thermoelectric module and making the about 35 °C temperature-difference of those can obviously enhance the performance of in terms of its voltage, its thermoelectric figure of merit ZT and output power of the thermoelectric modules.