A successful optimization of the electrospinning parameters for obtainment of biodegradable polyester urethane (DP) webs of fibers, neat and graphene oxide (GO) modified, was performed. The effect of the processing parameters (distance between the needle tip and the collector, applied voltage, and flowing rate), solution type and polymer concentration, on the fiber-forming process and the obtained fibers’ morphology was examined. The best homogeneity of the fibers was achieved for 12 wt% DP dissolved in 80:20 wt% mixture of chloroform and ethanol, applying similar processing parameters for the neat and modified samples (0.5 ml/h pumping rate, 15 kV applied voltage, and 150 mm distance to the collector, for the neat sample, and 0.4 ml/h, 18 kV, and 110 mm, for the GO modified samples). The main novelty of this work is the modification of DP with low quantities (0.5, 1.0 and 2.0 wt%) of GO – the “next generation” nanomaterial for stem cell control. The morphological characterization revealed a fibrous microstructure consisting of randomly oriented fibers with a diameters ranging from hundreds nanometers to couple micrometers, representing a feasible imitation of the structure of extracellular matrix (ECM). The XRD studies showed high dispersion of GO in DP matrix and even exfoliation for the sample that contains 2 wt% GO. Raman studies neatly complemented the highest filler/matrix interactions and the superior levels of dispersion for this sample. TGA was used to analyze the thermo-oxidative degradation and also to determine the actual content of GO present in the samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.