Abstract
In this work we present a new type of scaffold obtained by solid-state reaction, simultaneous sintering of a mixture of precursor oxides, carbonates, and organic substances, the latter used for pore generation. Having variable local composition, exhibits excellent overall physicochemical and bioactivity response. Open porosity is about 50%-60% and its permeability 10-11 m2 . X-ray diffraction exhibits the presence of a sodium-calcium silicate and sodium-calcium phosphate crystalline phases. Additionally, by mechanical compression tests the range of failure stress obtained for the scaffolds was 0.3-1.1MPa. The bioactivity and dissolution rate of the scaffolds were evaluated by in vitro tests. After 1week soaking in simulated body fluid, the formation of a continuous hydroxyapatite layer, which does not differentiate local compositions, was observed. Our results from cell culture tests clearly indicate that during hydroxyapatite layer formation, scaffolds do not liberate any cytotoxic substances. Moreover, cells seeded in the hydroxyapatite-covered scaffolds grew better than the control.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Biomedical Materials Research Part B: Applied Biomaterials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.