Abstract
AbstractA method for fabricating epoxy resin films dispersing the surface‐modified barium titanate (BT) particles (BT‐epoxy resin composite films) are proposed. BT particles with a size of 7.8 nm and a crystal size of 8.6 nm were synthesized with a complex alkoxide method. To introduce epoxy groups on the BT particle surface, the BT particles were surface‐modified with 2‐(3,4‐epoxycyclohexyl)‐ethyltrimethoxysilane. A precursor solution, which was prepared by prereacting 2,2‐bis(4‐glycidyloxyphenyl)propane (BGPP) and phthalic anhydride in 4‐butyrolactone and adding the surface‐modified BT particles to the prereacting solution, was spin‐coated on glass substrates to fabricate the composite films. An increase in BT volume fraction in film increased dielectric constant of the composite film while keeping dissipation factor below 0.03. The dielectric constant attained 10.8 at a BT volume fraction of 30% in film that was around twice higher than pure epoxy resin film. POLYM. COMPOS., 31:1179–1183, 2010. © 2009 Society of Plastics Engineers
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.