Fabrication modulation of lignin-derived carbon nanosphere supported Pd nanoparticle via lignin fractionation for improved catalytic performance in vanillin hydrodeoxygenation

Abstract

Nano-lignin presents great potential in advanced carbon materials preparation since it integrates the advantages of nanomaterials as well the preferable properties of lignin (e.g. high carbon content and highly aromatic structure). Herein, lignin-derived carbon nanosphere supported Pd catalysts (Pd@LCNS) were prepared via a two-step carbonization of Pd2+ adsorbed lignin nanospheres (LNS) and applied in vanillin hydrodeoxygenation. The effect lignin heterogeneity on the synthesis of Pd@LCNS as well as its catalytic performance was further investigated through the synthesis of Pd@LCNS using three lignin fractions with different molecular weight. The results showed that the three Pd@LCNSs exhibited significant differences in the morphology of both carbon support and Pd nanoparticles. Pd@LCNS-3 prepared from high molecular weight lignin fraction (L-3) presented stable carbon nanosphere support with the smallest particle size (∼150 nm) and the highest Pd loading amount (3.78 %) with the smallest Pd NPs size (∼1.6 nm). Therefore, Pd@LCNS-3 displayed superior catalytic activity for vanillin hydrodeoxygenation (99.34 % of vanillin conversion and 99.47 % of 2-methoxy-4-methylphenol selectivity) at 90 °C without H2. Consequently, this work provides a sustainable strategy to prepare uniformly dispersed lignin-based carbon-supported Pd catalyst using high molecular weight lignin as the feedstock and further demonstrate its superior applicability in the selective transfer hydrogenation of vanillin.