Abstract
In this work, the Zn/Al composite coating was prepared on the surface of Q345 steel using arc spraying. The simple and efficient cold-pressing technique was used for the composite coating. The cold pressure sealing (CPS) technique is proposed to reduce the porosity of the composite coating. The corrosion behavior of Zn/Al composite coatings without and with cold pressure sealing treatment in a corrosive environment was studied. The microstructures of composite coatings without and with CPS were studied by scanning electron microscope (SEM), and the corrosion properties of composite coating without and with CPS were comparatively investigated. The results showed that the porosity of the composite coating was significantly reduced to 2% by CPS. After 28 days of immersion, the dense corrosion products filled the defect area in the CPS sample. After CPS treatment, the corrosion potential is −0.829 V, and the corrosion current density is 5.636 × 10−6 A/cm2. After cold pressing, the bonding strength of the coating is 13.82 MPa, which is 43% higher than that before the sealing treatment. The Zn/Al composite coating treated by CPS exhibits excellent corrosion resistance in the simulated marine environment.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.