Abstract
Tetragonal copper ferrite nanoparticles were fabricated by a thermal-treatment method by using a solution that contained poly(vinyl alcohol) (PVA) as a capping agent and Cu and Fe nitrates as alternative sources of metal. Heat treatment was conducted at temperatures between 673 and 823K, and final products had different crystallite sizes ranging from 11 to 42nm. The influence of calcination temperature on the degree of crystallinity, morphology, microstructure, and phase composition was investigated by different characterization techniques, i.e., X-ray diffraction (XRD), transmission electron microscopy (TEM), field emission scanning electron microscope (FESEM), and Fourier transform infrared (FT-IR) spectroscopy, respectively. The compositions of the samples were determined by energy dispersion X-ray analysis (EDXA), which revealed the presence of Cu, Fe, and O in the samples. The formed nanoparticles exhibited ferromagnetic behavior with unpaired electrons spins, which was confirmed by using a vibrating sample magnetometer (VSM) and electron paramagnetic resonance (EPR) spectroscopy.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call