Abstract
(YbxY0.90−xLa0.10)2O3 (x=0.01–0.10) transparent ceramics were fabricated and their structural properties were investigated. The XRD showed our samples exhibited single cubic Y2O3 phase. The lattice parameters were refined with the Rietveld method. The compact structure and an average grain size of 40–50μm were revealed by the microstructure. The local fine structure around Yb ions was investigated by using the XAFS (X-ray absorption fine structure) technique. The results showed that: the local structure around Yb ions in the samples with different concentration of Yb ions was basically similar, and Yb ions replaced Y position to form the solid solution. The Yb ions were trivalent. With the concentration of Yb2O3 increased, the coordination number (N) and first shell Yb–O bond length (R) decreased, and the degree of disorder (σ) increased.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.