Aluminium composite materials are exponentially growing up and rapidly gaining importance because of their properties like low density, high strength, high stiffness, environmental resistance, low co-efficient of thermal expansion etc. In this context aluminum-boron carbide composites, with 2.5, 5 and 7.5 wt% of boron carbide (B4C) particulate reinforced, were prepared by stir casting process and the effect of the percentage of reinforcement of B4C on dry sliding wear and friction coefficient were investigated. The wear tests were carried out on a pin-on-disc type apparatus at a linear speed of 1m/s, sliding distance of 500 m and a constant load of 30 N. The coefficient of friction was recorded on line. Wear rates were calculated from mass loss measurements. Scanning electron microscope was used to examine the tribo-surface of worn Al- B4C composites. The results showed that the wear rate of 7.5 wt% B4C composites is 0.375 mg/min which is significantly lower than pure Al alloy (3.125 mg/min). The friction coefficient decreases from 0.477(for pure Al alloy) to 0.261(for 7.5 wt% B4C composites).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Surface Engineering and Interdisciplinary Materials Science
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.