Abstract
N-type Bi2Te3 based thermoelectric compound was prepared by spark plasma sintering with a temperature range of 340~460°C and powder size of ~75㎛, 76~150㎛, 151~250㎛. Thermoelectric properties of the compound were measured as a function of the sintering temperature and powder size. With increasing sintering temperature, the electrical resistivity and thermal conductivity of the compound greatly changed because of the increase in relative density. The Seebeck coefficient and electrical resistivity were varied largely with increasing powder size. Therefore, the compound sintered at 460°C, with the powder of ~75㎛, showed a figure of merit of 2.44 x 10-3/K. Also, the bending strength was 75MPa.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.