Abstract
AbstractIn order to fully pump and smoothen the temperature gradient of the gain medium, multistage gradient doping Yb:YAG laser ceramics were designed. The composite green bodies were fabricated by tape casting, and multistage gradient doping Yb:YAG ceramics with high optical quality were prepared by vacuum sintering and hot isostatic pressing. For samples pre‐sintered at 1740°C for 30 h and then HIP‐ed at 1700°C for 3 h in argon at 200 MPa, the in‐line transmission values at 1100 nm of YAG, 0.6 at.%Yb:YAG, and 1.5 at.%Yb:YAG ceramics were found to be 83.9%, 84.1%, and 83.3%, respectively. Finally, the 940 nm laser diode was used as the pump source to realize the 1030 nm laser output of multistage gradient doping Yb:YAG ceramic slab with a total energy of 3.43 J. The corresponding optical‐to‐optical conversion and slope efficiencies were 30% and 45%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.