Abstract
This paper focuses on novel iron-based soft magnetic composites synthesis utilizing low friction factor parylene C films to coat iron powder via chemical vapor deposition polymerization. The morphology, magnetic properties, density, and chemical stability of parylene insulated iron particles were investigated. The coated parylene insulating layer was characterized by scanning electron microscopy and energy dispersive X-ray spectroscopy. The thickness of parylene C film is averagely 300 nm according to the results of transmission electron microscopy. Parylene C film uniformly coated the powder surface resulting in reducing the permeability imaginary part, increasing electrical resistivity and increasing the operating frequency of the synthesized magnets. It was shown that the parylene C coated compacts exhibited noticeably higher density compared to the epoxy resin coated compacts at the same pressure, suppress at 800 MPa increased the density by 17.02%. The result of Tafel curves indicated that the resistance of the iron particles to corrosion by NaCl solution is obviously improved after being insulated with parylene C film.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.