Abstract
Carbon fiber reinforced silicon carbide composites (Cf/SiC) were derived through precursor infiltration pyrolysis route (PIP) at 1600°C in vacuum atmosphere using polysiloxane as precursor. The matrix of Cf/SiC was characterized by X-ray diffraction and elemental analysis. The results show that crystalline β-SiC can be derived at 1600°C in vacuum from polysiloxane. The flexural strength and fracture toughness of polysiloxane derived from Cf/SiC can reach up to 70 MPa and 2.3MPa·m respectively1/2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.