Abstract
Transparent ceramics are at the heart of modern magneto-optical materials providing promising opportunities for Faraday isolators. 1.0 at% RE:Tb3Ga5O12 (rare earth (RE) = Pr, Tm, Dy) transparent ceramics were successfully prepared by air sintering and sequential HIP technique using the coprecipitated powders as the raw material. All the powders have shown to be a pure cubic terbium gallium garnet (TGG) phase and exhibit good dispersion. Additionally, a change could not be observed in particle shape with the different doped ions. After the two-step sintering, all the obtained ceramics have good optical quality, and the in-line transmittances at 1070 nm are higher than 80%. Moreover, no secondary phase can be detected from the microstructures. However, the pores which remain entrapped in the ceramics can be noted. The Verdet constant of ceramic samples is optimized by RE doping, and the Verdet constant at 632.8 nm is about −143 rad·T−1·m−1, which is about 5% higher than that of TGG ceramics. Finally, the thermo-optical properties of 1.0 at% RE:TGG transparent ceramics are compared. The annealed TGG ceramic showed the best thermo-optical properties, and the thermally induced depolarization of 1.0 at% Ce:TGG and 1.0 at% Tm:TGG was inferior to that of annealed TGG ceramic.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.