Abstract
Abstract In this study, transparent LaErZr2O7 ceramic with high excess La and Er contents (nominally La1.28Er1.28Zr2O7.84) was successfully prepared by vacuum sintering at 1850 °C for 6 h using nanosized powder. The XRD, SEM, EDX and TEM results reveal that the single pyrochlore phase in the powder sample transforms to the coexistence of La-rich pyrochlore phase and Er-rich defect fluorite phase after high temperature sintering. The high excess amounts of La and Er favor the formation of pyrochlore structure. Despite the coexistence of two phases, the sample with 1 mm thickness shows excellent in-line transmittance in the visible to mid-infrared region (as high as 81% at 1100 nm). The upconversion and infrared emission under 980 nm exciting were measured and discussed as well.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.