Abstract
An amorphous single phase and coexistent amorphous and hcp-Mg phases in the Mg-Zn-La system were found to form in the composition ranges of 20 to 40%Zn and 0 to 12%La and 12 to 20%Zn and 0 to 4%La, respectively. The hcp phase has an ellipsoidal morphology and the particle size and interparticle distance are in the range of 5 to 10 nm and 3 to 10 nm, respectively. The mixed phase alloys exhibit high mechanical strength combined with good ductility and the tensile strength (σ B ) and fracture elongation (∈ f ) at 288 K are 675 MPa and 4.3% for Mg 85 Zn 12 La 3
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.