Abstract
We analyze and compare the differences in the dewetting phenomena and crystal structure between Ag(5.0 nm) and Au(5.0 nm) layers deposited on a Ti(1.0 nm) seed layer coated onto a MgO(001) substrate. The samples are deposited at room temperature and annealed at 350-450 °C for 5 h. The surfaces of both Ag/Ti and Au/Ti films exhibit a completely separated island structure, subsequently leading to the formation of a nanodot array after annealing. Based on atomic force microscopy (AFM) analysis, we conclude that the dewetting progression speed of Ag/Ti films is higher than that of Au/Ti films. Based on X-ray diffraction (XRD) results, the Ti thin film acts as a seed layer, assisting the epitaxial growth of fcc-Ag(001) nanodots on the MgO(001) substrate, whereas in the case of Au/Ti, the Au layer grows non-epitaxially on the MgO(001) substrate, which is related to the difference in the surface energies of Ag and Au. Furthermore, the optical absorbance spectra of the self-organized Ag and Au nanodots with the Ti seed layer are obtained in the visible light range and the optical properties of Ag and Au nanodots are compared.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.