Abstract
This study aims at synthesizing porous coconut ash (CA)-based geopolymer foam with high thermal insulation property. Sodium hydroxide (NaOH), alumina slag (AS) and water contents as the main parameters, which affect the performance hardened CA, have been studied. The porosity was developed by hydrogen gas resulted from the interaction of Al metal, in AS, with NaOH. The compressive strength, bulk density, porosity and thermal conductivity were evaluated. The results proved that the AS has a potential impact on the reduction of thermal conductivity of CA-based geopolymer foam by creation of high porous system. Open celled hardened CA-based geopolymer with high porosity (∼87%), low thermal conductivity (∼0.045 W/m·K), compressive strength (1.3 MPa) and bulk density (∼0.60 g/cm3) was obtained when 7% AS (by weight of CA powder) and water to CA powder ratio of 0.4 were used.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.