Fabrication and characterization of silica ceramic compact prepared using Aloe‐Vera mucilage as a binder

Abstract

AbstractIn this study, silica compacts were fabricated through a powder processing route at different compaction pressure, using Aloe‐Vera (AV) mucilage as a binder. The silica compacts were prepared at 90, 100, and 110 MPa compaction pressure using 0%–16 wt% of AV binder. The optimum amount of AV binder was 14 wt% for both 90 and 100 MPa and 12 wt% for 110 MPa. The maximum achieved green density and green strength of silica compacts at the optimum binder amount were 62.3% and 4 MPa, respectively at 110 MPa compaction pressure. The green silica compacts prepared at 110 MPa compaction pressure exhibited a minimum porosity of 21% and maximum flexural strength of 15 MPa after sintering at 1400°C. The green silica compacts with the optimum amount of binder were strong enough for machining. The Fourier transform infrared spectroscopy analysis revealed the functional groups present in AV mucilage. The binder burnout characteristic of AV mucilage in the silica compact was determined by thermogravimetric analysis and differential thermal analysis. Additionally, AV gel acted as a binder and solvent simultaneously for ceramic compaction.