Abstract
Two biobased composite films have been prepared with poly (lactic acid-trimethylene carbonate), polylactic acid and Laponite by solvent evaporation method. The 1H NMR and FTIR spectrums illustrate that P (LA-TMC) polymer is successfully synthesized and designed composite films are produced. Morphometric analyses demonstrate that the roughnesses of the film's surface and cross-section are on the increase with higher PLA and Laponite content. Mechanical performances reveal that the rise in tensile strength and modulus while maintaining excellent elongation at break is mainly due to the increase in the content of polylactic acid and Laponite. By utilizing the nano effect of Laponite, the maximum tensile strength of the composite film reaches 34.59 MPa. Thermal property results illustrate that the Tg and initial decomposition temperature are on the growth with the increase of PLA content. However, it is not significant on the effect of Laponite on the initial decomposition temperature. The water vapor permeability measurements prove that the barrier property of P(LA-TMC)/PLA/Laponite composite film is on the ascent with the Laponite addition. Hydrolytic degradation tests indicate that PLA and Laponite play avital part in accelerating the degradation rate of composite films and alkaline media is superior acidic and neutral conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Biological Macromolecules
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.