Abstract
The aim of this study was to produce bulk nanocrystalline Al/Al12(Fe,V)3Si alloys by mechanical alloying (MA) and subsequent hot pressing (HP) of elemental powders. A nanostructured Al-based solid solution was formed by MA of elemental powders for 60 h. After HP of the as-milled powders at 550°C for 20 min, the Al12(Fe,V)3Si phase was precipitated in a nanocrystalline Al matrix. Scanning electron microscopy (SEM) images of the bulk samples represented a homogeneous and uniform microstructure that was superior to those previously obtained by rapid solidification-powder metallurgy (RS-PM). Nanostructured Al-8.5Fe-1.3V-1.7Si and Al-11.6Fe-1.3V-2.3Si alloys exhibited high HV hardness values of ∼205 and ∼254, respectively, which are significantly higher than those reported for the RS-PM counterparts.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Minerals, Metallurgy, and Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.