Abstract
AbstractBACKGROUND: This work focuses on combining electrospun biodegradable poly‐DL‐lactide (PDLLA) fibres and 45S5 Bioglass® for tissue engineering applications.RESULTS: A variety of fibrous structures were produced upon application of an electric field to a flowing solution of PDLLA (5 wt/v%) in di‐methyl carbonate (DMC). Electrospinning was achieved at an applied voltage of 8.5 kV for a fixed flow rate of 5 µL min−1. Scanning electron microscopy images of PDLLA fibres deposited on 45S5 Bioglass® sintered pellets revealed that the fibres had diameters in the range 100–200 nm, leading to increased surface roughness, as assessed by white light interferometry. Bioactivity studies on PDLLA fibre coated Bioglass® substrates were carried out in simulated body fluid (SBF) for 7, 14 and 28 days. It was found that mineralization of PDLLA fibres on 45S5 Bioglass® substrate (formation of hydroxyapatite) occurred after 7 days of immersion in SBF and full coverage of PDLLA fibres with HA nanocrystals was achieved after 14 days in SBF.CONCLUSION: The approach investigated represents a convenient method to develop a controlled mineralized fibrous topography on bioactive glass substrates for improved cell attachment, which can be exploited in bone tissue engineering applications. Copyright © 2009 Society of Chemical Industry
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Chemical Technology & Biotechnology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.