Abstract
Magnesium (Mg) has a great potential to be used in various field of work since it is lightweight and has low density properties. However, its application is limited due to its poor properties for Mg has a relatively low strength. Improvement is made by mixing Mg with calcium (Ca) as composite element for it is lightweight and non-toxic. In this research, Mg is prepared with different weight percentage (0, 0.5, 1, 1.5, 2 wt. %) of Ca with pure Mg as reference prepared by powder metallurgy (PM) method to study the mechanical properties. Morphological analysis carried out by optical microscope shows increase grain refinement with the increase of calcium content in Mg-Ca composites. The phase transition upon addition of Ca is determined using XRD method detects formation of Mg2Ca. Range from 1.78 g/cm3 to 1.83 g/cm3, the density of each sample composite increase. While porosity profiles show inverse characteristics upon addition of Ca. Microhardness strengths also intensifies up to 193.20 MPa as more Ca content added in.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call